| Werk-stoff N° | DIN | NBN | ASTM | SAE | BS | AFNOR | Toestand | Rm in N/mm2* | Re in N/mm2 (σ0.2) | σb in N/mm2 | Rek A % | E in N/mm2 x 103 | Hardheid in HB |
|
Austenitisch roestvaststaal
|
|||||||||||||
|
1.4301
|
X5CrNi1810
|
304
|
304S15
|
Z6CN1809
|
600
|
195
|
45
|
200
|
120-
180 |
||||
|
1.4306
|
G-X6CrNi189
|
304L
|
304S12
|
Z2CN1810
|
470
|
180
|
45
|
200
|
130-200
|
||||
|
1.4404
|
X2CrNiMo1810
|
316L
|
316S12
|
Z3CND1910M
|
590
|
190
|
40
|
200
|
120-
180 |
||||
|
1.4401
|
X5CrNiMo17222
|
316
|
316S16
|
Z6CND17.11
|
610
|
200
|
40
|
200
|
130-180
|
||||
|
Aluminium volgens DIN 1725
|
|||||||||||||
|
3.2151.01
|
G-AlSi6Cu4-225
|
SGAlSi6Cu4
|
319.0
|
326
|
AS5U
|
G
|
150
|
90
|
1
|
60
|
|||
|
G-AlSi5Mg-235
|
SGAlSi7
|
356.0
|
323
|
AS7G
|
G
|
140
|
80
|
2
|
55
|
||||
|
G-AlSi7Mg-235
|
SGAlSi7Mg
|
A356.0T6
|
336
|
A-S7G03Y23
|
G
|
240
|
180
|
2
|
75
|
||||
|
G-AlSi12-230
|
SGAlSi12
|
LM6
|
AS13
|
G
|
160
|
70
|
4
|
50
|
|||||
|
3.3206
|
AlMgSi0,5
|
6060
|
A-GS
|
||||||||||
|
3.2315
|
AlMgSi1
|
6082
|
A-SGM0,7
|
||||||||||
|
Hardheid in HB10
|
|||||||||||||